SAMURAI Carbon fabric SY-24k 70 g/m² (plain, IM) 100 cm

Технические характеристики

USA: width 39.37", weight 2.1 oz/yd²

Plain weave

Width 100 cm

Fiber: Tenax® IMS 60 24k

IM-Carbon fibers (Intermediate modulus) are specifically suited for lightweight applications. In comparison with standard Carbon fibres as type HTS oder T 300, the IM-fiber provides ca. 20 % increased tensile modulus and ca. 30 % increased tensile strength at a higher elongation at break.

"Lightweight, strong, black!"

This fabric is made by Sakai Ovex / Japan for R&G. It increases the performance and reduces the weight of your composites as well as enhancing the surface finish making the composites aesthetically appealing.

Unlike other tissues, Samurai™ Carbon fabric is delivered without binder application, so that it can deform relatively well. The fabric is very delicate, the fibers can be moved easily if mistreated.

Should it be slip-resistant, it can be fixed by applying a spray adhesive like Aerofix 2. As an alternative it could be wet-out on a polyethylene film prior to cutting, to improve its handling.

This fabric is characterized by:

• Reduced weight by 20% or more
• Increased mechanical performance
• Superior surface finish
• Unique aesthetic look

Usable width 100 cm, delivered with taped edge with approx. 103 cm width. Supplied on paper carrier.

Technical data:
24k-yarn spread to 24 mm
Tensile strength: 5600 MPa
Tensile modulus: 290 GPa
Elongation at break: 1.9 %
Density: 1.8 g/cm³
Fibre diameter: 5 µm.

Please note:
For technical reasons, we can´t deliver this article in rolls of 10, 20 and 100 meters.