TeXtreme® carbon fabric, 76 g/m² (PW, IM, bias cut) 100 cm

Технические характеристики

USA: width 39.37", weight 2.2 oz/yd²

Bias cut

Plain weave, width 100 cm
Tape width 20 mm

Fibre: Torayca® M 30 SC 18k / intermediate modulus

IM-Carbon fibers (Intermediate modulus) are specifically suited for lightweight applications. In comparison with standard Carbon fibres as type HTS oder T 300, the IM-fiber provides approx. 20 % increased tensile modulus and approx. 30 % increased tensile strength at a higher elongation at break.

Technical data:
Tensile strength: 5490 MPa
Tensile modulus: 294 GPa
Elongation at break: 1,9 %

Calculated data for hand laminates with 35 volume percent fibres:
Resin consumption: 54,6 g/m²?, laminate thickness: 0,076 mm laminate weight: 130,6g/m²

TeXtreme® Spread Tow Fabric (STF) increases the performance and reduces the weight of your composites as well as enhancing the surface finish making the composites aesthetically appealing. The material is pliable and easy to handle when forming and cutting. TeXtreme® is available in a variety of areal weight and fiber type configurations.

The specified tissue weight increases by the binder to about 9 g/m³ .

Key benefits of TeXtreme®:

• Reduced weight by 20% or more
• Increased mechanical performance
• Superior surface finish
• Unique aesthetic look
• Easy to handle and cut due to a stable structure

More Information:
Storing: Dry and below 30 °C
UV: No sensitivity
Shelf life: No limitation
EP-Binder: 18 °C softening takes place (improved processing at room temperature)

Please note:
Due to the manufacturing process sporadical "weaving defects" can occur, mostly consisting of warp joints. These are labelled with coloured tape on the fabric itself as well as on its edge. It´s possible to remove this labelling with the use of heat (heat gun) without leaving any residue. We guarantee a free of defects roll up to 3 m length.

Information about bias cut eWiki.