TeXtreme® Carbon fabric 64 g/m² (PW, HT, bias cut) 100 cm

Технические характеристики

USA: width 39.37", weight 1.9 oz/yd²

Bias-cut

Fibre type: Tenax® UTS 50 S 12k, tape width 25 mm

Calculated data for hand laminates with 35 volume percent fibres:
Resin consumption: 46 g/m², laminate thickness: 0.064 mm, laminate weight: 110 g/m²

R&G now offers bias-cut fabrics, which are mainly used in the model aircraft as torsion reinforcement in wings and fuselages. It is not the fabric which is produced diagonally, but the beginning and end of a roll are cut at an angle of 45 °. This reduces the waste to a minimum and so also large areas can be realized even with small roll sizes.

TeXtreme®

TeXtreme® Spread Tow Fabric (STF) increases the performance and reduces the weight of your composites as well as enhancing the surface finish making the composites aesthetically appealing. The material is pliable and easy to handle when forming and cutting. TeXtreme® is available in a variety of areal weight and fiber type configurations.

Key benefits of TeXtreme®:

• Reduced weight by 20% or more
• Increased mechanical performance
• Superior surface finish
• Unique aesthetic look
• Easy to handle and cut due to a stable structure

More Information:
Storing: Dry and below 30 °C
UV: No sensitivity
Shelf life: No limitation
EP-Binder: 18 °C softening takes place (improved processing at room temperature)

Please note:
Due to the manufacturing process sporadical "weaving defects" can occur, mostly consisting of warp joints. These are labelled with coloured tape on the fabric itself as well as on its edge. It´s possible to remove this labelling with the use of heat (heat gun) without leaving any residue.
We do guarantee a free of defects roll up to 3 m length.