Технические характеристики
High core material for industrial applications with a fine cell structure
Specification:
Closed cell foam PMI (polymethacrylimide, IG-F = Fine industrial grade, high performance core material for sandwich components
• Superior mechanical properties
• High heat distortion temperature and solvent resistance
• Thermoformable
• At low temperatures, low thermal conductivity
• Low thermal conductivity at low temperatures
• Very good strength values
• Very good dielectric properties
• Very good X-ray transparency
• Less resin absorption due to finer cell structure
• Natural colour white
Applications:
Automotive engineering: high-strength cabs (truck bodywork)
Medical engineering: X-ray treatment tables
Others: Sports articles, model construction, SMC parts sports aircraft construction
Technical data:
Apparent density (DIN 53420): 52 kg/m³
Compressive strength (DIN 53421): 0,9 MPa
Tensile strength (DIN 53455): 1,9 MPa
Shear strength (DIN 53294): 0,8 MPa
Modulus of elasticity (ISO 527-2): 70 MPa
Shear modulus (DIN 83294): 19 MPa
Heat distortion temperature (DIN 53424): 180 °C
In 1mm, 2 mm and 3 mm thickness available.